- A Basic Study on the Fabrication of W-M(M=Cu, Sn, Ni) System High Density Composite (I)
-
Tak-Soon Jang, Jun-Hee Hong, Tae-Haeng Lee, Jar-Myung Koo, Chang-Bin Song
-
J Korean Powder Metall Inst. 2009;16(4):268-274.
-
DOI: https://doi.org/10.4150/KPMI.2009.16.4.268
-
-
17
View
-
0
Download
-
2
Citations
-
 Abstract
 PDF
- For the purpose of obtaining basic information on the development of lead-free materials, a high density composites (a) W-Cu, (b) W-Sn (c)W-Cu-Sn and (d) W-Cu-Ni were fabricated by the P/M method. The particle size of used metal powders were under 325 mesh, inner size of compaction mould was phi8 mm, and compaction pressure was 400 MPa. A High density composite samples were sintered at a temperature between 140°C and 1050°C for 1 hour under Ar atmosphere. The microstructure, phase transformation and physical properties of the sintered samples were investigated. As the results, the highest relative density of 95.86% (10.87 g/cm3) was obtained particularly in the sintered W-Cu-Sn ternary system sample sintered at 450 for 1hr. And, Rockwell hardness (HRB) of 70.0 was obtained in this system.
-
Citations
Citations to this article as recorded by  - Fabrication and Performance Analysis of Environment Friendly Double Core Bullets for Small Arms
Jun-Hee Hong, Tak-Soon Jang, Chang-Bin Song, Dae-Wha Kang
Journal of the Korea Institute of Military Science and Technology.2011; 14(3): 345. CrossRef - Design and Performance Analysis of Environment Friendly Double Core Bullets for Small Arms
Jun-Hee Hong, Tak-Soon Jang, Chang-Bin Song, Byung-In Kim
Journal of the Korea Institute of Military Science and Technology.2011; 14(2): 264. CrossRef
|
kpmi